Standard Characteristics of Mn-Zn Materials

Material μiac tanδ/μiac αμγ Bms Hc Tc ρ d Specifications
10kHz 10kHz
x10-5
20-60°
x10-6
1200A/m
(mT)
(A/m) (°C) (Ω-m) (kg/m3)
x103
2H1
15000
0.95 0.17 350 2.3 105 0.06 5.0
2E2B
10000
0.34 0.28 390 6.0 120 0.047 4.9
2H2A
10000
-20°:9000min
1.1 1.3
(20-70°)
370 2.5 105 1.1 4.9
2G1
7000
0.54 0.41 410 6.0 135 0.02 4.8
2G4
5300
0.1 0.28 460 6.0 160 1.30 4.9
2H4A
4300
0.06 0.5 420 4.0 155 0.4 4.8
2H4G 4000 0.1 0.19 427 4.7 185 2.3 4.8 PDF 45KB
2H5
3700
0.19
-0.09
410 6.5
170
2.2 4.7
2G8
2300
0.26
(100kHz)
2.8
520 9.0
>200
13 4.8 PDF 100KB
2N5
1900

0.123 0.055 460 7.5 >260 11.1 4.7 PDF 53KB
2H8
1700
0.26
(100kHz)
2.0
500 15.5
>250
11 4.8
2H6
800
1.3
(500kHz)
0.4
490 22
>200
2.3 4.8

Standard Characteristics of Ni-Zn Materials

Material
μiac
tanδ/μiac
αμγ
Bms
Hc
Tc
ρ
d
Specifications

X10-5
(MHz)
20-60°
X10-6
(mT)
(A/m)
(A/m)
(°)
(Ω-m)
(Kg/m3)
x103
3A7
2000
0.9
0.1
2.8
280
1200
12
100
104
5.2
3A8
1500
0.4
0.05
4
310
1200
13
135
103
5.2
3A6
1400
0.78
0.1
3
300
1200
15
110
>106
5.1
2K
1100
5
0.1
5
370
1500
20
>150
104
5.1
3A4
800
1.8
0.1
15
350
1200
16
130
>106
5.0
3A5
630
0.9
0.1
10.3
350
1200
15
160
>106
5.1
3A
600
1.4
0.2
3
300
1200
50
140
>106
5.1
3K
600
3.5
0.1
9
450
4000
28
>250
>102
5.1
4A3
400
2.6
0.5
1.7
290
1200
80
150
>106
5.1
4D4
400
2
0.5
12
350
1200
51
185
>106
5.0
D12A
260
7.1
0.5
40
370
1200
80
240
>106
5.1
5K
250
10
0.1
10
490
12000
80
>250
104
5.1
5B3
120
9
5
28
300
1200
110
>250
103
4.9
6D8
73
9.8
10
11
290
1200
240
>250
>106
5.1
6D2
60
14
10
30
325
1200
280
>250
>106
5.1
6B2
30
32
20
70
350
12000
520
>250
>106
5.1
7B2
13
70
50
85
240
8000
2270
>250
>103
5.1

The Values were obtained from testing methods carried out in accordance with JIS-C2561:General Testing Methods for Cores Made of Ferromagnetic Oxides.

All the characteristics specified as above are the criteria, not guarantee values.